防腐工艺对钢铁零件耐盐雾性的影响

文章出处(chu):广东欧洲杯app下载 大地(di)化(hua)工(gong)有限公司 人气:-发表时间:2016-11-13 10:24:00

防止(zhi)钢铁腐(fu)蚀的工(gong)(gong)艺有(you)很多,最常(chang)用(yong)的防腐(fu)工(gong)(gong)艺是在金(jin)属(shu)表(biao)面涂(镀)非金(jin)属(shu)和金(jin)属(shu)保护层,或通(tong)过特殊的工(gong)(gong)艺处理在其表(biao)面形成(cheng)一层化(hua)学转化(hua)保护膜。

根据(ju)构成保护层的物(wu)质,可以(yi)分为以(yi)下 3 类。

◆非金(jin)属(shu)(shu)保(bao)护层:把有机和无机化合物涂覆(fu)在金(jin)属(shu)(shu)表(biao)面。

◆金(jin)属(shu)保(bao)护层:在钢(gang)铁表面涂(镀)一种金(jin)属(shu)或(huo)合金(jin)作(zuo)为保(bao)护层,以减慢腐蚀速度。 用作(zuo)保(bao)护层的金(jin)属(shu)或(huo)合金(jin)通(tong)常(chang)有锌、锡、铝、镍、铬、铜及各种合金(jin)等。

◆热(re)镀:将被保(bao)(bao)护的(de)金(jin)(jin)属(shu)材料或制品浸渍(zi)在熔(rong)融的(de)金(jin)(jin)属(shu)中,使(shi)其表面形(xing)(xing)成(cheng)一(yi)层保(bao)(bao)护性金(jin)(jin)属(shu)覆盖层。能形(xing)(xing)成(cheng)液(ye)态的(de)金(jin)(jin)属(shu)一(yi)般(ban)是相对(dui)低熔(rong)点、耐蚀(shi)、耐热(re)的(de)金(jin)(jin)属(shu),如 Al、Zn 等(deng)。通过化(hua)(hua)学(xue)或电化(hua)(hua)学(xue)方法形(xing)(xing)成(cheng)的(de)化(hua)(hua)学(xue)保(bao)(bao)护层也称(cheng)化(hua)(hua)学(xue)转化(hua)(hua)膜。 根据成(cheng)膜时所(suo)采(cai)用的(de)介质(zhi),可将化(hua)(hua)学(xue)转化(hua)(hua)膜分为氧化(hua)(hua)物膜、磷酸盐膜、铬酸盐膜等(deng)。

拖拉(la)机中含有(you)各种不同(tong)的结(jie)构(gou)件(jian)和铸件(jian),其防腐性(xing)能(neng)直(zhi)接(jie)关系产(chan)品的质量。 拖拉(la)机及工(gong)程机械产(chan)品传(chuan)统的防腐工(gong)艺多采用(yong)涂漆(qi)或电镀工(gong)艺,但(dan)此(ci)类(lei)工(gong)艺对使用(yong)中存在“相(xiang)对运(yun)动”的零件(jian)、受挤压零件(jian)和容易磕碰(peng)的零件(jian)防腐保护效果较差,如何解决此(ci)类(lei)零件(jian)的防腐保护,是(shi)许多企业面临的问题。

在相关资料报(bao)道中,用(yong)(yong)(yong)标准板采(cai)用(yong)(yong)(yong)不同涂(tu)装工(gong)艺(yi)(yi)(yi)进行耐(nai)盐雾性(xing)对比的(de)(de)较多(duo),而采(cai)用(yong)(yong)(yong)实际零件用(yong)(yong)(yong)不同种防腐(fu)(fu)(fu)工(gong)艺(yi)(yi)(yi)处理进行耐(nai)盐雾对比试验(yan)的(de)(de)报(bao)道较少 。本研究通过(guo)对几(ji)种常用(yong)(yong)(yong)防腐(fu)(fu)(fu)蚀工(gong)艺(yi)(yi)(yi)处理的(de)(de)实际钢铁零件进行耐(nai)盐雾试验(yan),对其结果进行分析研究,对提高产品的(de)(de)防腐(fu)(fu)(fu)能力具有参考(kao)意义。

欧洲杯app下载
大地行业动态

1、防腐处理工艺的选择

根(gen)据一般机械制造(zao)企(qi)业的(de)防(fang)(fang)(fang)腐(fu)蚀(shi)(shi)要(yao)求,选(xuan)取(qu)了常(chang)用(yong)的(de)10种典型防(fang)(fang)(fang)腐(fu)处(chu)理工艺(yi)进行(xing)耐(nai)盐雾腐(fu)蚀(shi)(shi)试(shi)验。根(gen)据常(chang)用(yong)防(fang)(fang)(fang)腐(fu)工艺(yi)耐(nai)盐雾腐(fu)蚀(shi)(shi)的(de)性能(neng)指标(biao),将试(shi)验时间定到最长(zhang)600H,试(shi)验中选(xuan)用(yong)的(de)冷轧板与冷轧零件材(cai)料相同。

不同(tong)防腐(fu)工艺(yi)所用(yong)的零件及(ji)腐(fu)蚀(shi)试验结果(guo)如表1 所示。

A 工艺:喷砂—浸涂铁红环氧底漆。 铸铁垫板经喷丸处理,表面粗糙度Ra50右,浸涂江苏某企业生产的黏度为18S的铁红环氧底漆,下文简称铁红环氧底漆。

B 工艺:喷砂—中温磷化—浸涂铁红环氧底漆。铸铁垫板经喷丸处理,表面粗糙度Ra50左右,于50℃中温锌系磷化,浸涂铁红环氧底漆。

C 工艺:喷砂—磷化—一般阴极电泳涂装。 铸铁垫板经喷丸处理,表面粗糙度Ra50左右,于50℃中温锌系磷化,表面电泳厚度为20μm的普通阴极电泳漆。

D工艺:喷砂—磷化—高边缘高防腐阴极电泳涂装。 铸铁垫板经喷丸处理,表面粗糙度Ra50左右,于50℃中温锌系磷化,表面电泳厚度为20μm的高边缘高防腐阴极电泳漆。

E工艺:喷砂—热镀锌。 铸铁垫板经喷丸处理,表面粗糙度Ra50左右,表面浸涂厚度为110μm的锌层。

F工艺:电镀锌。 表面电镀厚度为10μm 的锌层。

G工艺:铸件喷涂丙烯酸面漆。 表面喷涂厚度为20μm的丙烯酸磁漆。

H工艺:“热浸锌工艺[2]+喷面漆工艺” 处理与“电泳底漆+喷面漆工艺”。

I工艺:冷轧板—喷涂铁红环氧底漆。

J工艺:冷轧板—磷化—喷涂铁红环氧底漆。 表面先于50℃中温锌系磷化,再喷涂铁红环氧底漆。

2、试验结果对比分析

仅用(yong)铁(tie)(tie)红环氧底(di)漆(qi)浸涂铸(zhu)(zhu)(zhu)(zhu)件(jian)(jian)(jian)的(de)(de)(de)涂装工(gong)(gong)(gong)(gong)(gong)艺(yi)(yi)(yi)(yi)(yi)(yi)(yi)(yi)(yi)或仅喷(pen)涂面(mian)(mian)漆(qi),其抗(kang)蚀(shi)防(fang)锈能(neng)(neng)(neng)力(li)非常差(cha),如(ru)(ru)(ru) A 工(gong)(gong)(gong)(gong)(gong)艺(yi)(yi)(yi)(yi)(yi)(yi)(yi)(yi)(yi)和(he)(he)(he) G工(gong)(gong)(gong)(gong)(gong)艺(yi)(yi)(yi)(yi)(yi)(yi)(yi)(yi)(yi)。铸(zhu)(zhu)(zhu)(zhu)铁(tie)(tie)件(jian)(jian)(jian)与冷轧板(ban)采用(yong)同样(yang)的(de)(de)(de)涂装工(gong)(gong)(gong)(gong)(gong)艺(yi)(yi)(yi)(yi)(yi)(yi)(yi)(yi)(yi),对耐(nai)(nai)盐(yan)(yan)雾(wu)腐(fu)(fu)(fu)蚀(shi)能(neng)(neng)(neng)力(li)差(cha)别(bie)很(hen)大,冷轧板(ban)的(de)(de)(de)耐(nai)(nai)盐(yan)(yan)雾(wu)腐(fu)(fu)(fu)蚀(shi)能(neng)(neng)(neng)力(li)远优于(yu)(yu)铸(zhu)(zhu)(zhu)(zhu)铁(tie)(tie)件(jian)(jian)(jian)(如(ru)(ru)(ru) B 工(gong)(gong)(gong)(gong)(gong)艺(yi)(yi)(yi)(yi)(yi)(yi)(yi)(yi)(yi)和(he)(he)(he) J 工(gong)(gong)(gong)(gong)(gong)艺(yi)(yi)(yi)(yi)(yi)(yi)(yi)(yi)(yi))。 采用(yong)相(xiang)同的(de)(de)(de)防(fang)锈底(di)漆(qi),若都不进行(xing)磷(lin)(lin)(lin)化(hua)(hua)处(chu)理(li)(如(ru)(ru)(ru) A 工(gong)(gong)(gong)(gong)(gong)艺(yi)(yi)(yi)(yi)(yi)(yi)(yi)(yi)(yi)和(he)(he)(he) I 工(gong)(gong)(gong)(gong)(gong)艺(yi)(yi)(yi)(yi)(yi)(yi)(yi)(yi)(yi)),铸(zhu)(zhu)(zhu)(zhu)铁(tie)(tie)件(jian)(jian)(jian)耐(nai)(nai)盐(yan)(yan)雾(wu)腐(fu)(fu)(fu)蚀(shi)试(shi)验(yan)(yan) 24 h 即出现大面(mian)(mian)积锈蚀(shi),而(er)冷轧板(ban)到168 h 方(fang)出现局部起泡腐(fu)(fu)(fu)蚀(shi);若均进行(xing)磷(lin)(lin)(lin)化(hua)(hua)处(chu)理(li)(见 B工(gong)(gong)(gong)(gong)(gong)艺(yi)(yi)(yi)(yi)(yi)(yi)(yi)(yi)(yi)和(he)(he)(he) J 工(gong)(gong)(gong)(gong)(gong)艺(yi)(yi)(yi)(yi)(yi)(yi)(yi)(yi)(yi)),铸(zhu)(zhu)(zhu)(zhu)铁(tie)(tie)件(jian)(jian)(jian)耐(nai)(nai)盐(yan)(yan)雾(wu)腐(fu)(fu)(fu)蚀(shi)试(shi)验(yan)(yan) 168 h 即局部锈蚀(shi),而(er)冷轧板(ban)到 240 h 也没有(you)出现锈蚀(shi)现象。磷(lin)(lin)(lin)化(hua)(hua)工(gong)(gong)(gong)(gong)(gong)艺(yi)(yi)(yi)(yi)(yi)(yi)(yi)(yi)(yi)对提(ti)高(gao)铸(zhu)(zhu)(zhu)(zhu)铁(tie)(tie)件(jian)(jian)(jian)的(de)(de)(de)抗(kang)蚀(shi)防(fang)锈能(neng)(neng)(neng)力(li)影响非常大,磷(lin)(lin)(lin)化(hua)(hua)工(gong)(gong)(gong)(gong)(gong)艺(yi)(yi)(yi)(yi)(yi)(yi)(yi)(yi)(yi)可(ke)(ke)以(yi)较(jiao)大程度提(ti)升零(ling)件(jian)(jian)(jian)的(de)(de)(de)耐(nai)(nai)盐(yan)(yan)雾(wu)防(fang)腐(fu)(fu)(fu)能(neng)(neng)(neng)力(li)(如(ru)(ru)(ru) A 工(gong)(gong)(gong)(gong)(gong)艺(yi)(yi)(yi)(yi)(yi)(yi)(yi)(yi)(yi)和(he)(he)(he) B 工(gong)(gong)(gong)(gong)(gong)艺(yi)(yi)(yi)(yi)(yi)(yi)(yi)(yi)(yi))。 采用(yong)相(xiang)近(jin)的(de)(de)(de)涂装工(gong)(gong)(gong)(gong)(gong)艺(yi)(yi)(yi)(yi)(yi)(yi)(yi)(yi)(yi),铸(zhu)(zhu)(zhu)(zhu)铁(tie)(tie)件(jian)(jian)(jian)不经(jing)磷(lin)(lin)(lin)化(hua)(hua)处(chu)理(li)耐(nai)(nai)盐(yan)(yan)雾(wu)试(shi)验(yan)(yan) 24 h 即出现大面(mian)(mian)积锈蚀(shi),而(er)同样(yang)零(ling)件(jian)(jian)(jian)经(jing)磷(lin)(lin)(lin)化(hua)(hua)处(chu)理(li)后(hou)(hou),耐(nai)(nai)盐(yan)(yan)雾(wu)腐(fu)(fu)(fu)蚀(shi)试(shi)验(yan)(yan)达到 168 h 时,虽然也出现严重锈蚀(shi),但样(yang)板(ban)表(biao)面(mian)(mian)整(zheng)体状况(kuang)比没有(you)进行(xing)磷(lin)(lin)(lin)化(hua)(hua)处(chu)理(li)的(de)(de)(de)铸(zhu)(zhu)(zhu)(zhu)铁(tie)(tie)件(jian)(jian)(jian)要(yao)好很(hen)多(duo)。在涂膜(mo)不被磕碰损(sun)(sun)坏(huai)的(de)(de)(de)情况(kuang)下,采用(yong)高(gao)防(fang)腐(fu)(fu)(fu)高(gao)边缘阴(yin)极(ji)电泳(yong)(yong)漆(qi)可(ke)(ke)以(yi)满足铸(zhu)(zhu)(zhu)(zhu)铁(tie)(tie)件(jian)(jian)(jian)长期防(fang)锈技术要(yao)求。而(er)对于(yu)(yu)使(shi)用(yong)中存(cun)在零(ling)件(jian)(jian)(jian)间相(xiang)对运动或磕碰现象时,采用(yong)“热浸锌(xin)(xin)工(gong)(gong)(gong)(gong)(gong)艺(yi)(yi)(yi)(yi)(yi)(yi)(yi)(yi)(yi)+喷(pen)面(mian)(mian)漆(qi)工(gong)(gong)(gong)(gong)(gong)艺(yi)(yi)(yi)(yi)(yi)(yi)(yi)(yi)(yi)”,可(ke)(ke)以(yi)有(you)效(xiao)解决(jue)零(ling)件(jian)(jian)(jian)涂膜(mo)损(sun)(sun)坏(huai)面(mian)(mian)的(de)(de)(de)锈蚀(shi)问题(ti)(如(ru)(ru)(ru) H 工(gong)(gong)(gong)(gong)(gong)艺(yi)(yi)(yi)(yi)(yi)(yi)(yi)(yi)(yi)和(he)(he)(he) D 工(gong)(gong)(gong)(gong)(gong)艺(yi)(yi)(yi)(yi)(yi)(yi)(yi)(yi)(yi))。“热浸锌(xin)(xin)工(gong)(gong)(gong)(gong)(gong)艺(yi)(yi)(yi)(yi)(yi)(yi)(yi)(yi)(yi)”可(ke)(ke)以(yi)有(you)效(xiao)提(ti)高(gao)铸(zhu)(zhu)(zhu)(zhu)件(jian)(jian)(jian)的(de)(de)(de)抗(kang)蚀(shi)性(xing)能(neng)(neng)(neng),其抗(kang)蚀(shi)性(xing)要(yao)优于(yu)(yu)一般(ban)阴(yin)极(ji)电泳(yong)(yong)工(gong)(gong)(gong)(gong)(gong)艺(yi)(yi)(yi)(yi)(yi)(yi)(yi)(yi)(yi)(如(ru)(ru)(ru) E 工(gong)(gong)(gong)(gong)(gong)艺(yi)(yi)(yi)(yi)(yi)(yi)(yi)(yi)(yi)和(he)(he)(he) C工(gong)(gong)(gong)(gong)(gong)艺(yi)(yi)(yi)(yi)(yi)(yi)(yi)(yi)(yi)),铸(zhu)(zhu)(zhu)(zhu)铁(tie)(tie)件(jian)(jian)(jian)经(jing)热浸锌(xin)(xin)工(gong)(gong)(gong)(gong)(gong)艺(yi)(yi)(yi)(yi)(yi)(yi)(yi)(yi)(yi)处(chu)理(li)后(hou)(hou),耐(nai)(nai)盐(yan)(yan)雾(wu)时间600 h时仍(reng)没有(you)红锈出现。

电镀锌零件耐(nai)盐(yan)雾性要(yao)远(yuan)低于(yu)高(gao)边(bian)缘(yuan)(yuan)(yuan)阴极(ji)电泳(yong)(yong)(yong)防(fang)腐工(gong)艺(如 F 工(gong)艺和 D 工(gong)艺)。不同的(de)阴极(ji)电泳(yong)(yong)(yong)漆(qi)对铸(zhu)铁件的(de)抗蚀(shi)防(fang)锈能力(li)的(de)影(ying)响(xiang)很大(da)(如 C 工(gong)艺和 D 工(gong)艺)。 一(yi)般阴极(ji)电泳(yong)(yong)(yong)底漆(qi)铸(zhu)件耐(nai)盐(yan)雾腐蚀(shi)试验(yan) 96 h 出现局部锈蚀(shi),240h出现大(da)面(mian)(mian)(mian)积锈蚀(shi),而(er)采用(yong)高(gao)边(bian)缘(yuan)(yuan)(yuan)高(gao)防(fang)腐阴极(ji)电泳(yong)(yong)(yong),经 600 h盐(yan)雾腐蚀(shi)试验(yan),样(yang)板表(biao)(biao)面(mian)(mian)(mian)仅出现少(shao)量“点(dian)蚀(shi)”;主(zhu)要(yao)原因是(shi)普(pu)通电泳(yong)(yong)(yong)漆(qi)膜的(de)边(bian)缘(yuan)(yuan)(yuan)防(fang)锈性差,而(er)一(yi)般铸(zhu)铁件的(de)表(biao)(biao)面(mian)(mian)(mian)都比较粗糙,表(biao)(biao)面(mian)(mian)(mian)相当于(yu)存(cun)在(zai)无数(shu)的(de)“边(bian)缘(yuan)(yuan)(yuan)”,因此对于(yu)铸(zhu)件(特(te)别是(shi)表(biao)(biao)面(mian)(mian)(mian)粗糙度较高(gao)的(de)铸(zhu)件)必须选(xuan)用(yong)高(gao)边(bian)缘(yuan)(yuan)(yuan)防(fang)腐电泳(yong)(yong)(yong)涂(tu)料进(jin)行(xing)涂(tu)装。

磷化工艺和(he)高(gao)(gao)防腐高(gao)(gao)边(bian)缘(yuan)阴极电泳漆提高(gao)(gao)铸铁件耐盐雾腐蚀性能(neng)的影响主要因素为铸铁件成分和(he)表面粗糙(cao)度。

2.1成分的影响

铸件(特别是(shi)铸铁(tie)(tie)件)与(yu)一(yi)般碳(tan)素(su)(su)结(jie)构钢(GB/ T700—2006)化(hua)学(xue)成(cheng)分(fen)不同,其杂质含量(liang)是(shi)碳(tan)素(su)(su)铸铁(tie)(tie)主要是(shi)以机械性(xing)能高低来判定(ding)其是(shi)否合(he)格,国(guo)标对(dui)(dui)其化(hua)学(xue)性(xing)能没有统一(yi)的(de)(de)要求,但不同企业规定(ding)了本企业对(dui)(dui)铸铁(tie)(tie)化(hua)学(xue)成(cheng)分(fen)的(de)(de)参(can)考(kao)值。从表 2 和表 3 对(dui)(dui)比可以看(kan)出,铸铁(tie)(tie)的(de)(de)碳(tan)(C)、硫(S)、磷(P)等(deng)非(fei)铁(tie)(tie)元素(su)(su)含量(liang)均要大于碳(tan)素(su)(su)钢,大约差1 个(ge)数(shu)量(liang)级。 这(zhei)些非(fei)铁(tie)(tie)元素(su)(su)的(de)(de)存在(zai)导致铁(tie)(tie)分(fen)子很容(rong)易(yi)与(yu)它们(men)形(xing)成(cheng)无(wu)数(shu)的(de)(de)原(yuan)电(dian)(dian)池(chi),产生电(dian)(dian)化(hua)学(xue)腐蚀(shi)。 在(zai)相同的(de)(de)温度(du)条件下,电(dian)(dian)化(hua)学(xue)腐蚀(shi)的(de)(de)速度(du)要远大于化(hua)学(xue)腐蚀(shi)。

2.2表面粗糙度的影响

铸件的表面粗糙度一般在 Ra12?5 以上,有的铸铁件表面粗糙度可达 Ra25,甚至Ra50。 而碳素结构钢表面粗糙度一般在Ra3?2 以下,热轧的表面粗糙度一般在 Ra6?3~12?5。 粗糙度大,一方面更容易加快凝结水和CO2的附着,促使腐蚀的发生;另一方面,表面粗糙度也影响表面涂层的覆盖保护。如果仅在铸件表面涂覆一层铁红环氧底漆,由于涂料本身的流平性,在铸件粗糙面的突出部分很难形成有效的涂层保护膜。铸铁零件经磷化工艺处理后,其表面形成的磷化膜会有效吸附涂料等保护物,从而在粗糙面的突出部位也能形成一层磷化膜加电泳漆的保护膜。经磷化工艺处理的铸铁件表面再涂装高边缘电泳漆,会在其表面形成由磷化膜和电泳涂膜组成的多重复合保护层,从而达到较好的防护效果。


欧洲杯app下载
大地行业动态


3、结语

通(tong)过对几种钢铁防腐(fu)(fu)工艺耐盐雾检测结(jie)果的(de)(de)对比研究,说明不同(tong)防腐(fu)(fu)工艺对钢铁零(ling)件防腐(fu)(fu)性(xing)能的(de)(de)影响非常(chang)大,在(zai)实际(ji)工作中应(ying)根据产品的(de)(de)使(shi)用环境和需要选择不同(tong)的(de)(de)防腐(fu)(fu)蚀工艺。

在防腐(fu)(fu)(fu)性能要(yao)求相同(tong)的(de)(de)(de)情况下,铸(zhu)铁零件(jian)(jian)(jian)需要(yao)采(cai)用(yong)比冷轧(ya)钢铁材(cai)(cai)料防腐(fu)(fu)(fu)能力更强的(de)(de)(de)防腐(fu)(fu)(fu)处(chu)理工(gong)(gong)(gong)艺(yi)(yi)(yi)(yi)。而(er)采(cai)用(yong)相同(tong)的(de)(de)(de)防腐(fu)(fu)(fu)工(gong)(gong)(gong)艺(yi)(yi)(yi)(yi)处(chu)理的(de)(de)(de)零件(jian)(jian)(jian),材(cai)(cai)质(zhi)为铸(zhu)铁的(de)(de)(de)零件(jian)(jian)(jian)防腐(fu)(fu)(fu)性能要(yao)远低于材(cai)(cai)质(zhi)为冷轧(ya)钢板(ban)材(cai)(cai)质(zhi)的(de)(de)(de)零件(jian)(jian)(jian)。对于在装配(pei)和使用(yong)中容易(yi)被磕碰(peng)、磨(mo)损(sun)、存(cun)在相对运(yun)动的(de)(de)(de)产(chan)品(pin)(pin)或(huo)零件(jian)(jian)(jian),采(cai)用(yong)一(yi)般的(de)(de)(de)涂装工(gong)(gong)(gong)艺(yi)(yi)(yi)(yi)或(huo)电镀工(gong)(gong)(gong)艺(yi)(yi)(yi)(yi)均(jun)难以满足防腐(fu)(fu)(fu)要(yao)求,建议(yi)采(cai)用(yong)热镀锌或(huo)热渗锌防腐(fu)(fu)(fu)工(gong)(gong)(gong)艺(yi)(yi)(yi)(yi),可(ke)以有效解决零件(jian)(jian)(jian)涂膜容易(yi)损(sun)坏(huai)锈蚀问题。对于铸(zhu)件(jian)(jian)(jian)(特别是(shi)产(chan)品(pin)(pin)表面(mian)粗(cu)糙(cao)度(du) Ra>25 的(de)(de)(de)产(chan)品(pin)(pin)),采(cai)用(yong)普通的(de)(de)(de)涂装工(gong)(gong)(gong)艺(yi)(yi)(yi)(yi)粗(cu)糙(cao)表面(mian)的(de)(de)(de)尖(jian)端部分不容易(yi)被涂覆,防腐(fu)(fu)(fu)效果较差,采(cai)用(yong)磷化和高边缘电泳涂装工(gong)(gong)(gong)艺(yi)(yi)(yi)(yi),可(ke)以大(da)大(da)提(ti)高其耐盐雾腐(fu)(fu)(fu)蚀性能。



广东欧洲杯app下载 大地化工有限公司是一家集研发,生产,销售,服务于一体的专业化技术型企业,公司致力于涂料新产品的研究和开发,针对市场变化及客户需要,不断开发出满足市场需求的新产品,公司不仅向客户提供优质产品,并将提供全方位的技术施工指导和员工培训服务.主营:水性工业漆,工业装备漆,2K卡车漆,原子灰-咨询热线:0757-28878287

此文关键字:新闻资讯,仿古艺术漆,闪光漆,砂纹漆